Pengaruh Radiasi UV Buatan Terhadap Kerusakan Permukaan Bahan Isolasi Resin Epoksi Silane

Yanolanda Suzantry H, Suharyanto Suharyanto

Abstract


Abstract—Polymer is now developed as the material replacement of the porcelain isolator and glass insulators. However, tropical climates and high rainfall can cause problems to its. Ultraviolet radiation will continuously accelerate to the surface of the polymer insulator material. As a result, the surface of the insulating material becomes easier letting electric current flow and a fast formation of extensive damage to the surface of the insulator material. Materials used in this study were made from epoxy resin diglycidyl ether of bisphenol-A (DGEBA) as the base material, metaphenylen diamine (MPDA) as the reinforcement material and silica sand. DGEBA and MPDA composition was 30% silica sand filler 30%, 25%, 20%, 15%, 10% and 10% silicone rubber was 15%, 20%, 25%, 30%. The size of the test material was 120 mm x 50 mm x 5 mm. The study was conducted in the laboratory according to standard IEC 587: 1984. This study was conducted to determine the effect of ultraviolet radiation on hydrophobic contact angle and surface damage on the broad value of insulation material epoxy resin silanes. The results showed that the length of exposure time to UV light tended to increase the value of the contact angle. This was due to exposure to artificial UV rays which would accelerate the degradation process. The longer the level of ultraviolet radiation on the sample accelerating the degradation off silane epoxy resin insulators in addition, it caused greater leakage current on extensive damage to the surface of the insulating material.

Intisari— Material polimer saat ini dikembangkan sebagai pengganti material isolator porselin dan gelas. Tetapi pemasangan di daerah beriklim tropis dan bercurah hujan tinggi dapat menimbulkan permasalahan. Radiasi sinar ultraviolet secara terus menerus akan mempercepat terjadinya proses degradasi. Akibatnya permukaan bahan isolasi menjadi lebih mudah mengalirkan arus listrik dan cepat terbentuknya luas kerusakan permukaan pada bahan isolator. Bahan yang digunakan pada penelitian ini adalah resin epoksi yang terbuat dari diglycidyl ether of bisphenol-A (DGEBA) sebagai bahan dasar, metaphenylen diamine (MPDA) sebagai bahan pengeras dan diberi bahan pengisi sealant dan pasir silika. Komposisi bahan DGEBA dan MPDA dibuat sama yaitu masing-masing 30% sedangkan bahan pengisi pasir silika 30%, 25%, 20%, 15%, 10% dan silicone rubber 10%, 15%, 20%, 25%, 30%. Ukuran bahan uji adalah 120 mm x 50 mm x 5 mm. Penelitian dilakukan di laboraturium menurut standar IEC 587 : 1984. Penelitian ini dilakukan untuk mengetahui pengaruh radiasi sinar ultraviolet terhadap sudut kontak hidropobik dan nilai luas kerusakan permukaan pada bahan isolasi resin epoksi silane. Hasil penelitian menunjukkan bahwa lamanya waktu pemaparan sinar UV cenderung membuat nilai sudut kontak suatu bahan semakin kecil dan arus bocor pada permukaan bahan akan semakin meningkat sehingga mempercepat terbentuknya luas kerusakan permukaan.

Kata Kunci— Sinar UV, Sudut Kontak, Luas Kerusakan Permukaan, silane,pasir silika.


Full Text:

PDF

References


Berahim, Hamzah, “Metodologi Untuk Mengkaji Kinerja Isolasi Polimer Resin Epoksi Silane Sebagai Material Isolator Tegangan Tinggi di Daerah Tropis”, Disertasi,Universitas Gadjah Mada, Yogyakarta, 2005.

Wahada, Giyarhadi, “Pengaruh Sinar Ultraviolet Terhadap BahanIsolasi Resin Epoksi Dengan Pengisi Pasir Silica Dan Lem Silicone Rubber Terkontaminasi Polutan Parangtritis”, Tugas Akhir, Jurusan Teknik Elektro Fakultas Teknik UGM, Yogyakarta, 2003.

Hakim, Muhammad Arief Rahman, “Studi Pengaruh UV Terhadap Karakteristik Bahan Isolasi Resin Epoksi Berpolutan Garam (NaCl) Dengan Bahan Pengisi Pasir Silika Dan Lem Silikon”, Tugas Akhir, Jurusan Teknik Elektro Fakultas Teknik UGM, Yogyakarta, 2003.

Syakur, Abdul., Anggraini, Ika Novia., Sarjiyah., Hamzah Berahim, “Pengaruh Komposisi Bahan Isolasi Resin Epoksi dengan Bahan Pengisi Silicone Rubber terhadap Proses Tracking dan Erosi”, Universitas Gadjah Mada, Yogyakarta, 2010.

BS 5604:1986, IEC 587:1984, “Methods for Evaluating resistance to tracking and erosion of electrical insulating materials used under severe ambient conditions”, British Standards Institution, British standard (BS).

Hakim, Muhammad Arief Rahman, “Electrical Degradation and Breakdown I Polymer, IEE Material and Device Series”, England, 2003.

Nurlailati, Abdul Syakur, Sarjiya, Hamzah Berahim, Relationship Between Contact Angle and Stoichiometry Value On Epoxy Resin Polymer Insulating Materials, CTEE, Universitas Gadjah Mada, Yogyakarta, 2010.

Lee, Henry, Kris Neville, Epoxy Resins Their Applications And Technology, McGraw-Hill Book Company, INC, Newyork Torondo London, 1957.

Tobing, Bonggas L., Peralatan Tegangan Tinggi, PT. Gramedia Pustaka Utama, Jakarta, 2003.

Arismunandar A., Teknik Tegangan Tinggi, Pradnya Paramita, Jakarta., 1984.




DOI: http://dx.doi.org/10.22146/jnteti.v2i4.104

Refbacks

  • There are currently no refbacks.


Copyright (c) 2016 Jurnal Nasional Teknik Elektro dan Teknologi Informasi (JNTETI)

JNTETI (Jurnal Nasional Teknik Elektro dan Teknologi Informasi)

Departemen Teknik Elektro dan Teknologi Informasi, Fakultas Teknik Universitas Gadjah Mada
Jl. Grafika No 2. Kampus UGM Yogyakarta 55281
+62 274 552305
jnteti@ugm.ac.id